Degradation due to X-ray Flux
Many polymers suffer degradation (damage) after the X-ray Flux forces chemical bonds to break or re-arrange.
Polymeric Hydrocarbons lose Hydrogen to form C=C double bonds
These sp2 double bonds appear at slightly lower BE than sp3 single bonds.
Polymeric Hydrocarbons lose Hydrogen to form C=C double bonds
These sp2 double bonds appear at slightly lower BE than sp3 single bonds.
Degradation of Polymers due to Monochromatic and Non-Monochromatic X-rays